The purpose of this study is to investigate environmental effects on low cycle fatigue crack growth of SUS316. Low cycle fatigue test and periodical observation on inner surface of a hollow specimen was conducted by developing new type of replica observation. The crack growth in PWR environment was measured and the investigation of environmental effects on crack initiation and propagation was conducted. Crack initiation rate of fatigue test in PWR environment is faster than in air condition. Crack pr...
英字タイトル:
Environmental Effect on Low Cycle Fatigue Crack Growth of SUS316

The purpose of this study is to investigate environmental effects on low cycle fatigue crack growth of SUS316. Low cycle fatigue test and periodical observation on inner surface of a hollow specimen was conducted by developing new type of replica observation. The crack growth in PWR environment was measured and the investigation of environmental effects on crack growth was conducted. Crack initiation rate of fatigue test in PWR environment is faster than in air condition. Crack initiation is estimated ...
英字タイトル:
Environmental Effect on Low Cycle Fatigue Crack Growth of SUS316

The purpose of this study is to generalize P-curve for strain range condition focusing on crack initiation life and crack growth life. The fatigue tests under different constant strain range conditions were conducted in air and the observation of fatigue cracks on specimen surface was also conducted. Using data derived from experiment, dispersion of cry using two-parameter Weibull distribution. Furthermore, the relationship between strain range and shape parameter or scale parameter of crack initiation mo...
英字タイトル:
Study on fatigue crack initiation model in air for type 316 stainless steel

The purpose of this study is to investigate environmental effects on low cycle fatigue crack growth rate of SUS316 in different strain rate condition. The fatigue tests were conducted under different strain rate (0.4%/sec and 0.004%/sec) in simulated PWR environment with interrupting tests and the surface of specimens was observed. By the investigation of fatigue cracks growth, the effect of strain rate on crack growth rate was evaluated. From the results of tests, the followings were confirmed; ・Fatigu...
英字タイトル:
Influence of Strain Rate on Fatigue Crack Growth in SUS316 under Reactor Coolant Environment

Numbers of nuclear power plants have been operating for more than 30 years and some of them exceeding 40 years in Japan. In these ageing plants, fatigue evaluation has a significant measure in assuring the plant reliability. The environmental fatigue in light water reactors, which was first recognized in the 1980's in Japan, has been drawing attention worldwide because it may cause remarkable effects on the life of important components. The Japanese nuclear industries developed the world's first pract...
英字タイトル:
Environmental Fatigue Evaluation in PLM Activities of PWR plant

Numbers of nuclear power plants have been operating for more than 30 years and some of them exceeding 40 years in Japan. In these ageing plants, fatigue evaluation has a significant measure in assuring the plant reliability. The environmental fatigue in light water reactors, which was first recognized i n the 1980's in Japan, has been drawing attention worldwide because it may cause remarkable effects on the life of important components.. This paper int roduces a few examples of environmental fatigue evalu...
英字タイトル:
Environmental Fatigue Evaluation in PLM Activities of PWR plant

A fatigue damage assessment procedure based on crack growth prediction was shown, in order to quantify the risk for failure of nuclear power plant components. First, crack initiation and growth behavior during low-cycle fatigue tests was reviewed and it was shown that the fatigue life could be estimated by predicting the crack growth without considering incubation period before the crack initiation. The change in crack size with the number of cycles was obtained by using the equivalent stress intensity...
英字タイトル:
Fatigue Damage Assessment Procedure based on Crack Growth Prediction

To prevent degradation at Nuclear Power Plants (NPPs) by maintenance activity, fatigue evaluation should be improved to be more accurate. Studies of crack growth under equi-biaxial fatigue which is caused by thermal stress have been conducted for these purposes. Previous study shows that crack growth rate under equi-biaxial stress is faster than under uniaxial one. But the comparison is not quantitative. In this study, the difference of crack growth rate between equi-biaxial and uniaxial is confirmed q...
英字タイトル:
Study on the Behavior of Fatigue Crack Growth of Austenitic Stainless Steel under Equi-biaxial Stress

We have developed a new index called Resilience index, which evaluate the reliability of system safety of nuclear power plant under severe accident by considering the capability to recover from the situation the system safety function was lost. In this paper, a detailed evaluation procedure for the Resilience index was described. System safety of a PWR plant under severe accident was then assessed according to the Resilience index concept to discuss applicability of the index. We found that the Resilie...
英字タイトル:
Fundamental Study on Applicability of Resilience Index for System Safety Assessment

１．はじめに 事故時における原子力発電所の安全確保上重要なのは、一時的に喪失した安全機能をアクシデントマネジメント(AM)によりいかに早く必要なレベルまで回復できるかにある。そこで、原子力発電所の事故時における安全機能の信頼度を経年変化と保全の効果を取り入れて簡易かつ定量的に評価するため「レジリエンス指標」が提案され、その策定手法の開発が進められている。[1] 本研究では、レジリエンス指標を活用するため、低サイクル疲労による構造物損傷確率モデルを作成し、静的劣化要因に対する機器信頼性評価への適用性について......
英字タイトル:
Study on Reliability Analysis for Degradation of Static Components in the Application of Resilience Index